Table I Chemical composition of filler (mass%)
- | Si | Fe | Mn | Mg | Cr | Ti | Zr | Remarks | |
Filler | a | 0.06 | 0.15 | 0.61 | 4.80 | 0.10 | 0.11 | <0.01 | Standard wire (5183) |
b | 0.06 | 0.15 | 0.58 | 4.77 | 0.07 | 0.08 | 0.11 | Zr addition | |
c | 0.03 | 0.05 | 0.59 | 4.73 | 0.07 | 0.10 | 0.13 | High purity and Zr addition | |
d | 0.03 | 0.05 | 0.58 | 4.80 | 0.07 | 0.11 | <0.01 | High purity | |
e | 0.06 | 0.15 | 0.60 | 5.49 | 0.07 | 0.11 | <0.01 | High Mg |
- | Si | Fe | Mn | Mg | Cr | Ti | Zr | |
Base Metal | 0.08 | 0.19 | 0.64 | 4.82 | 0.06 | 0.01 | 0.00 | |
Weld Metal | A | 0.07 | 0.16 | 0.63 | 4.77 | 0.08 | 0.06 | 0.00 |
B | 0.07 | 0.16 | 0.62 | 4.77 | 0.07 | 0.05 | 0.05 | |
C | 0.06 | 0.13 | 0.64 | 4.80 | 0.07 | 0.05 | 0.05 | |
D | 0.06 | 0.13 | 0.62 | 4.72 | 0.06 | 0.05 | 0.00 | |
E | 0.07 | 0.17 | 0.63 | 5.00 | 0.07 | 0.06 | 0.00 |
Table III Result of tensile test
- | - | Yield Strength (MPa) |
Tensile Strength (MPa) |
Elongation (%) |
Reduction of Area (%) |
|
Base metal | 293K 77K 20K 4K |
143 159 166 179 |
300 424 536 557 |
25.9 36.9 25.6 28.7 |
39.3 28.2 24.9 27.4 |
|
Weld metal |
A | 293K 77K 20K 4K |
131 162 191 196 |
283 407 425 446 |
29.4 33.6 12.2 14.6 |
37.6 26.0 14.6 15.1 |
B | 293K 77K 20K 4K |
130 164 - 196 |
283 408 - 422 |
29.2 35.7 - 12.3 |
38.2 26.1 - 13.6 |
|
C | 293K 77K 20K 4K |
130 164 - 195 |
281 412 - 428 |
30.9 38.0 - 12.3 |
43.4 28.9 - 13.5 |
|
D | 293K 77K 20K 4K |
128 162 190 193 |
280 409 424 438 |
29.5 38.0 14.3 13.4 |
43.8 29.0 15.5 14.7 |
|
E | 293K 77K 20K 4K |
133 168 - 198 |
290 406 - 425 |
30.0 26.9 - 12.5 |
43.5 21.3 - 13.7 |
Table IV Result of Charpy impact test and JIC test
- | - | Absorbed Energy (J) |
JIC (kPa*m) |
KIC (MPa*(m)1/2) |
|
Base metal | 293K 77K 4K |
33.3 22.7 20.8 |
54.6 71.2 25.8 |
65.3 79.3 47.6 |
|
Weld metal |
A | 293K 77K 4K |
30.6 12.0 9.4 |
65.3 60.0 14.2 |
71.3 72.7 35.6 |
B | 293K 77K 4K |
29.0 11.8 9.5 |
57.9 53.9 13.6 |
67.2 68.9 34.7 |
|
C | 293K 77K 4K |
36.0 13.8 9.3 |
80.8 64.1 12.9 |
79.3 75.2 33.9 |
|
D | 293K 77K 4K |
36.9 13.3 8.8 |
83.1 53.0 13.4 |
80.4 68.3 34.5 |
|
E | 293K 77K 4K |
28.5 9.3 7.2 |
55.7 39.0 11.1 |
65.9 58.7 31.4 |