Table 1 Chemical compositions of austenitic stainless steels (wt%).
Type | C | Si | Mn | P | S | Cr | Ni | Mo | N | Fe |
304 | 0.060 | 0.59 | 1.01 | 0.018 | 0.009 | 18.33 | 8.35 | - | - | bal. |
304L | 0.019 | 0.43 | 0.90 | 0.032 | 0.004 | 18.40 | 9.11 | 0.18 | - | bal. |
316 | 0.040 | 0.48 | 0.66 | 0.010 | 0.002 | 17.10 | 10.05 | 2.02 | - | bal. |
310S | 0.060 | 1.24 | 1.53 | 0.002 | 0.009 | 24.63 | 20.21 | - | - | bal. |
JJ1 | 0.046 | 0.44 | 9.74 | 0.020 | 0.002 | 12.21 | 11.92 | 4.89 | 0.203 | bal. |
Table 2 Heat treatments for austenitic stainless steels.
Type | Solution-annealed | Sensitization | Desensitization |
304 304L 304(S) 304(SD) |
1373K-3.6ks 1310K-0.3ks 1373K-3.6ks 1373K-3.6ks |
973K-86.4ks 973K-86.4ks |
1193K-28.8ks |
316 316(S) 316(SD) |
1353K-3.6ks 1353K-3.6ks 1353K-3.6ks |
973K-86.4ks 973K-86.4ks |
1193K-28.8ks |
310S 310S(S) JJ1 |
1333K-3.6ks 1333K-3.6ks 1363K-10.8ks |
973K-172.8ks | - |