Table1 Specification of support collector
- | Anode | Cathode | |
Material | titanium fiber sintered plate |
stainless fiber sintered plate |
|
Virgin fiber size [mm] |
width | 0.05-0.1 | 0.012 |
length | 80 | 4-10 | |
Plate size [mm] |
thickness mean maximum minimum |
1.093 1.149 0.965 |
1.046 1.154 0.995 |
width | 270 | 270 | |
length | 1020 | 1020 | |
Porosity % | 60 | 70 | |
Surface treatment (thickness) |
platinum plating (3mm) |
gold plating (0.3mm) |
Table2 Species of ionexchange membrane
1.material
perfluorocarbon sulfonic acid resin(made in Japan)
2.size
Type No. |
Equivalent weight |
Thickness* [mm] (N=100) |
Width [mm] |
Length [mm] |
||
mean | maximum | minimum | ||||
B2 | 1,000 | 38 | 45 | 31 | 300 | 1050 |
B4 | 1,000 | 99 | 111 | 88 | 300 | 1050 |
A12 | 920 | 115 | 121 | 109 | 300 | 1050 |
Table3 Characteristics of membrane-electrode assemblies
No | Membrane | Anode loading (IrO2) [mg/cm2] |
Cathode loading (Pt) [mg/cm2] |
Thickness[mm] | Electrolysis* voltage [V] | ||||
mean | maximum | minimum | mean | maximum | minimum | ||||
1 | B2 | 3.6 | 3.0 | 67 | 87 | 52 | - | - | - |
2 | B4 | 3.6 | 3.0 | 126 | 140 | 114 | 1.541 | 1.563 | 1.528 |
3 | A12 | 3.6 | 3.0 | 148 | 174 | 127 | - | - | - |
Table4 Electrolysis performance of test manufactured 2500cm2 cell
Cell No |
Membrane | Temperature [°C] |
Current density [A/cm2] |
Cell voltage [V] |
Current efficiency [%] |
Energy efficiency [%] |
1 | B2 | 80 | 0.5 1 2 3 4 |
1.491 1.540 1.613 1.680 1.738 |
99.3 99.4 99.5 99.5 99.1 |
98.6 95.5 91.3 87.7 84.4 |
2 | B4 | 40 | 0.5 1 2 3 |
1.623 1.710 1.851 1.942 |
98.7 98.7 98.9 98.5 |
90.0 85.4 79.1 75.1 |
60 | 0.5 1 2 3 4 |
1.570 1.643 1.768 1.877 1.996 |
98.6 98.6 98.8 98.4 97.5 |
92.9 88.8 82.7 77.6 72.3 |
||
80 | 0.5 1 2 3 4 |
1.514 1.583 1.702 1.805 1.898 |
99.5 99.7 99.5 99.5 99.9 |
97.2 93.2 86.6 81.4 77.9 |
||
3 | A12 | 80 | 0.5 1 2 3 3.8 |
1.513 1.586 1.702 1.806 1.879 |
99.1 99.6 99.8 99.8 99.8 |
97.0 92.9 86.8 81.8 78.6 |